EXPLORING THE MECHANICAL PROPERTIES AND WEAR
RESISTANCE OF TRIP/TWIP MANGANESE STEELS
Tashbulatov Sherzod Baxtiyarovich
t.f.f.d., dots, Tashkent state technical university
tel: +998998006637
e-mail: t.sh.b.zohid@mail.ru
Yusupov Nuriddin Akmaljon ugli
PhD student, Andijan state technical institute,
tel: +998999016152
e-mail: nuriddin240497@gmail.com
https://doi.org/10.5281/zenodo.15645251
Abstract
This article explores the impact of stacking fault energy (SFE) on induced
plasticity, encompassing strain hardening, grain size hardening, solid solution
hardening, and precipitation hardening in manganese steel displaying
TRIP/TWIP phenomena .
It demonstrates how TRIP and TWIP influence the mechanical and sliding
wear characteristics of manganese steel, noting that TWIP enhances strength via
improved plasticity .
The study highlights the significant role of microalloying elements in
intermetallic precipitation, which enhances the steel's hardness and strength,
leading to improved sliding wear resistance in both lubricated and unlubricated
conditions .
Keywords
TRIP, Transformation Induced Plasticity; TWIP, Twinning Induced
Plasticity; SFE, Stacking Fault Energy; AHSS, Advanced High-Strength Steels.
1. Introduction
Manganese steels, known for their high toughness, strength, wear
resistance, and non-magnetic properties, are utilized in various applications due
to their work hardening capabilities .
The focus in the automobile industry is shifting towards Advanced High-
Strength Steels (AHSS) like TRIP and TWIP steels, aiming to reduce vehicle
weight while enhancing strength and toughness .
While ferrite steels offer high elongation, manganese steels can achieve
strengths up to 1.8GPa through Intermetallic precipitation and can improve
toughness and ductility via TRIP and TWIP mechanisms .
2. Intermetallic Precipitation and Strengthening Mechanism
ACADEMIC RESEARCH IN MODERN SCIENCE
International scientific-online conference
119
Intermetallic precipitation in steels is conducted after dissolving carbides
and nitrides in the austenite phase to avoid reducing the number of precipitates,
which would decrease strength .
Alloying elements like Nickel, Molybdenum, Niobium, Vanadium, and
Tungsten can form finer precipitates, leading to better refinement of
microstructures .
Larger precipitates can serve as nucleation sites for nanoprecipitation, and
hot-rolling enhances mechanical properties; however, rolling at higher
temperatures can lead to greater grain size and precipitate density .
3. TRIP/TWIP Steels
TWIP steels, characterized by high strain hardening, are promising
candidates for applications requiring multi-phase steel with austinites .
Alloying elements like Copper, Niobium, Chromium, Nickel, Titanium,
Vanadium, and Boron enhance mechanical and tribological properties; Copper
increases retained austenite, while Aluminum increases SFE for the TWIP effect .
Stacking fault energy (SFE) is crucial for induced plasticity: low SFE leads to
TRIP steels, intermediate SFE to TWIP steels, and high SFE to MBIP steels .
4. Mechanical Properties of TRIP/TWIP Steels
Young’s modulus in TRIP/TWIP steels is temperature-dependent,
decreasing as temperature drops below the Neel temperature, and carbon has
less impact on Young’s modulus in Fe-Mn-C steels .
Microalloying with Niobium increases yield and tensile strength but
decreases elongation in Fe-25Mn-3Si-3Al steel, while increased cold reduction
rolling and annealing temperature can increase nanoscale mechanical twins .
Cold rolling can significantly increase yield and ultimate tensile strength,
though elongation may be restricted, and TRIP steels can achieve ultimate
tensile strengths up to 1100 MPa with total elongation of 35–40% .
5. Influence of Elements on TRIP/TWIP Phenomenon
Vanadium promotes twinning activity, improving mechanical properties,
and can exhibit both TRIP and TWIP phenomena with high UTS, YS, and TE
when used in medium manganese steel processed via cold rolling and
intercritical annealing .
Carbon and Manganese are austenite stabilizers that enhances lattice
parameters and may cause severe segregation, while Silicon reduces Neel
temperature and increases solid solution hardening .
ACADEMIC RESEARCH IN MODERN SCIENCE
International scientific-online conference
120
Aluminium suppresses cementite precipitation, increases SFE, and delays
fracture, while Niobium and Molybdenum influence peak stress due to
precipitation and solid solution strengthening and can hinder grain growth .
6. Sliding Wear Assessment of Steels
Ageing treatments significantly reduced wear rate due to intermetallic
precipitates, and sintered samples of high vanadium high speed steel showed
optimal tribological capabilities .
TRIP phenomenon significantly improved hardness and work hardening,
while thermo-mechanically processed samples possessed better wear resistance
in comparison with as cast samples .
Micro alloying and heat treatments increases wear resistance and hardness
of the steel, and increased austenitization temperature results in higher yield
strengths and wear resistance .
7. Conclusion
Manganese steels are valued for their hardness, strength, and wear
resistance, making them suitable for applications in demanding environments,
with induced plasticity achieved by adjusting SFE values for TRIP, TWIP, and
MBIP .
TWIP steels benefit from annealing and deformation-induced twins, and
grain refining and precipitation hardening can further enhance strengthening
processes .
Microalloying elements like Niobium, Molybdenum, and Vanadium
significantly alter the TRIP/TWIP phenomena, leading to potentially greater
sliding wear resistance due to hardness, intermetallic precipitants, and induced
plasticity .
References:
1.
D.K. Matlock, J.G. Speer, Third Generation of AHSS: Microstructure Design
Concepts, Microstruct Texture Steels (2009).
2.
S. Keeler, M. Kimchi, P.J. Mooney, Advanced High-Strength Steels
Guidelines Version 6.0, WorldAutoSteel 6 (September) (2017) 314.
3.
M.K. Chowrasia, A. Kumar, M.K. Banerjee, U. Pandel, Effect of aging on
structure and properties of a transformation-induced plasticity-aided, J. Mater.
Eng. Perform. 13 (2019), https://doi.org/10.1007/s11665-020-04575-6.
4.
S.P. Neog, S. Das Bakshi, S. Das, Microstructural evolution of novel
continuously cooled carbide free bainitic steel during sliding wear, Wear 456–
457 (January) (2020), https://doi.org/10.1016/j.wear.2020.203359.
5.
S.P. Neog, S. Das Bakshi, S. Das, Effect of normal loading on microstructural
evolution and sliding wear behaviour of novel continuously cooled carbide free
ACADEMIC RESEARCH IN MODERN SCIENCE
International scientific-online conference
121
bainitic steel, Tribol. Int. 157 (2021) 106846, https://doi.org/10.1016/j.
triboint.2020.106846.
6.
D. Fernández-Valdés, A. Meneses-Amador, A. López-Liévano, A. Ocampo
Ramírez, Sliding wear analysis in borided AISI 316L steels, Mater. Lett. 285
(2021), https://doi.org/10.1016/j.matlet.2020.129138.